ZC-3111 Peroxide XLPE Insulation Compound for MV Cable Up To 35kV
This material is a kind of crosslinkable polyethylene insulation compound. It is made of high quality PE resin, dicumyl
peroxide agent and antioxidant agent by plasticizing granulation. Production process uses the closed system; Loss-in-
weight Feeder which guarantees stable precision of components. It has stable physical and chemical index and good
Application: 35kV crosslinkable cable insulation; Maximum working temperature is 90℃.
2. Technical Parameters
Elongation at break
Impact embrittlement performance@-76℃
Tensile strength variation
Breaking elongation variation
Hot prolongation@200℃, 0.2MPa,15min
Elongation under the load
Impurities Particle Size
Number of particles C1
Number of particles C2
Particles number<C1 qualified. BetweenC1 and C2, re-inspection. Particles number> C2, unqualified.
Recommend to use conventional extruder (three layers co-extrusion, draw ratio is from 20:1 to 30:1) and other
equipments need to be adjusted according to the circumstance.
Above temperature is only for reference.
keep at room temperature; Storage environment should be clean, dry and ventilated; Best use within six months from
the date of production.
5. Product packing
500kg in each package; Inner lined with plastic sealed film bag; Corrugated carton with tray at the bottom.